摘要: 通过Hummers法制备氧化石墨烯（graphene oxide ，GO），并通过共价修饰在其表面接枝靶向分子透明质酸（HA），得到氧化石墨烯-透明质酸（GO-HA）纳米载体。通过扫描电子显微镜（SEM），X射线衍射（XRD），红外光谱（IR）等手段分析GO的结构、组成和形貌。以透明质酸修饰的氧化石墨烯（GO-HA）作为水杨酸的药物运输载体，室温载药12h，平衡吸附量稳定在0.39左右。所以氧化石墨烯具有一定的载药能力。48997
毕业论文关键词：氧化石墨烯；透明质酸；纳米载体
Study on the preparation and properties of graphene oxide modified by hyaluronic acid
Abstract：Graphene oxide (oxide graphene, GO) was prepared by Hummers method and grafted on the surface of graphene oxide (GO-HA) by covalent modification on the surface of HA. By scanning electron microscopy (SEM), X - ray diffraction (XRD), infrared spectroscopy (IR) and other means to analyze the structure, composition and morphology of GO. As a drug delivery carrier for salicylic acid, the modified graphene oxide (GO-HA) with hyaluronic acid was used as the carrier, At room temperature for 12 hours of drug loading, the equilibrium adsorption capacity was stable at about 0.39 .Therefore, graphene oxide has a certain drug loading capacity.
KeyWords：graphene oxide, hyaluronic acid, nano microsphere
目录
1. 绪论 1
1.1 石墨烯 1
1.1.1 石墨烯的发现 1
1.1.2 石墨烯的制备方法 2
1.2 氧化石墨烯 3
1.2.1 氧化石墨烯的结构与性质 4
1.2.2 氧化石墨烯的制备方法 4
1.2.3 氧化石墨烯的医学应用 5
1.3 透明质酸 6
1.3.1 透明质酸的医学应用 6
1.4 实验仪器 6
1.4.1 X射线衍射仪 6
1.4.2 扫描电镜 7
1.4.3 红外光谱分析仪 7
1.4.4 紫外分光光度计 8
1.5 本课题研究目的及意义 9
2. 实验部分 9
2.1 实验原料与设备 9
2.1.1 实验原料 9
2.1.2 实验设备 10
2.2 实验方法 11
2.2.1 透明质酸修饰氧化石墨烯的合成 11
2.2.2 水杨酸的负载 11
2.2.3 XRD检测 11
2.2.4 SEM检测 12
2.2.5 纳米粒子的红外光谱检测 12
2.2.6 紫外光谱检测 12
3. 结果与讨论 12
3.1 纳米粒子的表征 13
3.1.1晶型分析 13
3.1.2 形貌分析 14
3.1.3 红外光谱分析 15
3.2 水杨酸标准曲线 16
3.2.1 进行透明质酸修饰对载药的影响 18
4．小结