摘要硝酸钾是一种强氧化剂，广泛应用于含能材料，各种点火药，是点火药主要组份之一（占点火药组份含量的70%以上）。硝酸钾进行超细化后，具有较大比表面积，与可燃剂的反应更完全、更彻底，因此可效提高点火药的燃烧性能。68583
本文使用扁平式气流粉碎机对硝酸钾（KNO3）进行粉碎， 对其最佳的粉碎条件进行了探究，制得平均粒径为4.7µm的超细硝酸钾（KNO3）粉体。本文还对硝酸钾（KNO3）超细粉碎过程中静电产生的原因进行了分析，并且提出静电积累的消除方法，从而使粉碎过程安全可靠。
毕业论文关键词 硝酸钾 , 气流粉碎 , 粒度 , 静电 , 安全
毕业设计说明书（论文）外文摘要
Title Study of ultrafine grinding method of potassium nitrate
Abstract
Potassium nitrate is widely used as a kind of Energetic Material, it is a kind of strong oxidizer, used for variety kinds of ignition powder, is one of the chief components of ignition powder (more than 70% of the content). After been ultrafine, it gets larger specific surface area, its reaction with combustible agent can be more completely and thoroughly, it can effectively enhance the combustion performance of gunpowder.
This article uses the flat type jet mill to make superfine powder of KNO3, to get the best grinding process conditions and the average obtained ultrafine KNO3 particle size is 4.7 μm. In this paper, the causes of electrostatic problem in the process of jet mill was analyzed, and put forward the method of eliminating electrostatic problem, so that the grinding process is safe and reliable.
Keywords Potassium Nitrate Jet Mill Particle Size Electrostatic Security
目 录
1 绪论 1
1.1 研究背景及意义 1
1.2 国内外研究概况 2
1.2.1国内外KNO3的超细化的研究 2
1.2.2 国内外KNO3的表面改性的研究 3
2 气流粉碎机的结构和粉碎机理 6
2.1气流粉碎机的结构 6
2.2粉碎机理 7
2.3 粉碎过程安全分析及防结块方法 7
2.3.1 静电的产生 7
2.3.2 避免静电方法 8
2.3.3 团聚产生的原因 8
2.3.4 防团聚措施 9
3 超细KNO3的制备 11
3.1实验原材料与设备 11
3.2实验方法 12
3.3实验结果与讨论 15
3.3.1气流压强对KNO3产品粒度的影响 15
3.3.2进料速度对产品粒度的影响 15
3.3.3 KNO3原料粒度对产品粒度的影响 16
3.3.4磨腔出料管高度对产品粒度的影响 17
3.4 实验结果 17