摘要二氧化钒是钒氧化物中最常见的一种氧化物,二氧化钒的相变温度在68℃左右,而且相变温度最接近室温,相变前后其结构会发生改变。正是因为二氧化钒的相变温度接近室温,且其在相变温度前后光学性质变化较明显,所以引起科学家们对其研究的兴趣。以二氧化钒薄膜为研究热点,在对二氧化钒相变原理和Material Studio中CASTEP有所了解的基础上,仿真不同温度下二氧化钒薄膜的特性,主要是其能带结构,光学特性,包括吸光系数和折射率,并根据相关公式计算出二氧化钒薄膜的透光率,并将计算出的结果与已在国际、国内刊物上发表过的结果对比分析,进行总结。64894
毕业论文关键词 二氧化钒; 相变; 光学性质
毕业设计说明书(论文)外文摘要
Title The Research of Transition of Vanadium oxide
Abstract
Vanadium dioxide is the most common form of vanadium oxides, the phase transition temperature of vanadium dioxide is at 68℃, which is closest to the room temperature and its structure will change during the phase transition. Because of this and its optical properties before and after the phase transition temperature obviously change, the scientists show interest in it. As vanadium dioxide the research focus, understanding the principles of the phase transition of vanadium dioxide and CASTEP in Material Studio. Simulate different temperature of vanadium dioxide properties, including band structure and optical properties (Absorption and Refraction) and work out the transmission of the vanadium dioxide. What’s more, compare the results with the results in journals in home and abroad and summarize.
Keywords vanadium dioxide; transition; the optical properties
目录
1 绪论 1
1.1 课题背景介绍 1
1.2 氧化钒薄膜的应用领域 2
1.2.1非制冷红外探测器 3
1.2.2 光开关及光存储 3
1.2.3 氧化钒薄膜在太赫兹领域的应用 4
1.3 本论文的研究意义、目的、内容 5
2 二氧化钒薄膜相变机理分析 7
2.1 二氧化钒薄膜相变机理 7
2.2 二氧化钒仿真理论 11
2.2.1 关于CASTEP 11
2.2.2 CASTAP 的任务 12
2.2.3 CASTAP能量任务 13
2.2.4 CASTAP几何优化任务 13
2.2.5 CASTAP动力学任务 15
2.2.6 CASTAP性质任务 15
2.3本章小结 16
3.二氧化钒薄膜相变理论计算 17
3.1 二氧化钒的模型建立 17
3.2 二氧化钒的电子态密度 18
3.3 二氧化钒的光学性质计算 19
3.3.1 吸光系数的模拟 20
3.3.2 折射率的模拟 21
3.3.3 透光率的计算 23
3.4 本章小结 24