摘要：针对20mm的厚板7A52高强铝合金，进行双面双TIG弧打底立焊和双脉冲MIG盖面焊焊接工艺试验的研究。大量焊接工艺试验结果表明，双面双TIG弧焊工艺参数为焊接速度15cm/min，交流焊接电流为275A时，焊缝成型良好,焊缝底部完全熔透焊缝表面光洁，无气孔、夹杂和热裂纹；双脉冲MIG盖面焊焊接工艺参数为焊接速度35cm/min或20.5cm/min，交流焊接电流为211A。焊缝整体抗拉强度为190MPa,是母材的46.3%。TIG焊接接头在焊缝处的硬度平均值比母材稍低；金相分析表明，打底焊与盖面焊焊接接头的焊缝为等轴晶，焊缝基体组织由α（Mg2Al）+β(Mg2Al3) 相组成。23424
关键词：7A52铝合金；双面双弧TIG焊；MIG盖面焊；宏观焊缝；微观组织
毕业设计说明书（毕业论文）外文摘要
Title The research on High strength Aluminum alloy Double-Sided Arc Welding
Abstract
The method of double-sided arc welding is used for welding20 mm thick 7A52 aluminum sheet is studied is this article. A large number of welding processes results showed that， high-quality welds can be achieved when process parameters are: welding speed at15cm/min, AC welding current is 275A; MIG welding process parameters are: welding speed at35cm/min or 20.5cm/min, AC welding current is 211A. The overall Weld tensile strength is 190MPa, about 46.3% of the base material.The average hardness of TIG welded joints is slightly lower the base material .Metallographic analysis showed that the weld metal is equiaxed grains, the weld matrix organization compose with α(Mg2Al) solid solution and β(Mg2Al3) phase .
Keywords 7A52 aluminum double-sided TIG welding MIG welding Macroscopic weld Microstructural
目次
1 绪论 5
1.1 背景 5
1.2 双面双弧焊 5
1.3 发展趋势 7
1.4 本课题研究的内容 7
2 双面双TIG弧对接焊接工艺方案设计与系统构建 8
2.1 双面双TIG弧对接焊接工艺设计 8
2.2 双面双TIG弧对接自动系统构建 9
2.3 金相组织分析过程 10
2.4 硬度测试 10
3 双面双TIG弧中厚板立焊焊接工艺试验研究 10
3.1 焊接试验方案 11
3.1.1 试验材料 11
3.1.2 接头形式 11
3.1.3 焊前处理 12
3.1.4 焊接操作要求 12
3.2 不同焊接电流双面双弧TIG焊接试验过程 14
3.3 7A52铝合金焊接接头焊缝微观组织分析 19
3.4 7A52铝合金焊接接头焊缝硬度分析 21
4 填充MIG焊接工艺试验研究 22
4.1 MIG焊接实验过程 24
4.2 焊接接头焊缝宏观形貌及缺陷分析 24
4.3 7A52铝合金焊接接头焊缝微观组织分析 26
4.4 焊接接头拉伸试验 27
结 论 29
致 谢 30
参考文献31
1 绪论
1.1 背景
铝合金因其密度小、比强度高、耐腐蚀、导电性好而且成形良好，而在交通运输、海洋工程及航空航天等方面的运用日益扩大。然而，铝合金在焊接过程中普遍拥有夹杂、气孔，软化、氧化和热裂纹等缺陷，这些问题对于焊接质量要求较高的车辆、船舶、航空航天飞行器都是亟待解决的。另外，铝合金焊接还广泛存在着强度不足、变形较大等较为严重的质量问题，因而研究铝合金的高效率、高质量的精密焊接就显得尤为重要。 高强铝合金双面双弧焊接工艺方法研究:http://www.751com.cn/cailiao/lunwen_16468.html