摘要试验研究了板厚为6mm的5083铝合金板的双面TIG焊接工艺，分析了接头组织及性能。结果表明，双面双弧TIG焊接可以形成外观良好的焊缝，适合的焊接参数为：电流为160A/80A，枪间距为0或5mm，弧长为5-6mm，焊速0.24m/min，送丝速度2m/min。接头的微观组织均匀，无明显缺陷。接头拉伸试验得到：屈服强度为母材的97%，抗拉强度为母材的88%。焊缝质量好，强度达到要求。6623
关键词  5083铝合金  双面双弧TIG焊接  拉伸试验  微观组织
毕业设计说明书（论文）外文摘要
Title    Investigation of Double-sided Double-wire Welding   for Spiral Pipe with Aluminium alloy                                                
Abstract
This study aimed to experimentally explore the microstructure and properties of joints undergoing double-sided TIG welding with 6mm thick aluminium alloy plates. The results show that double-sided TIG welding could fit the requirement of spiral pipe welding. The process window for double-sided TIG welding was obtained and the sound welds can be obtained under the condition of a welding speed of 0.24m/min, a welding current of 160A/80A, a distance of upper and lower torch ranged from 0 to 5mm, a distance from torch to plate range from 5 to 6mm, a wire feed rate of 2m/min. The joints had a fine microstructure and no conspicuous welding defects. Also, the average tensile strength of joints is 88% of base metal, and the average yield strength of joints is 97% of base metal.
Keywords  5083 aluminium alloy   double-sided TIG welding

目录
1 引言    1
1.1  课题背景及选题意义    1
1.2  铝合金焊接性分析    1
1.2.1  铝镁合金焊接特性    1
1.2.2  铝合金的焊接缺陷    2
1.2.3   铝合金缺陷的防止措施    3
1.3  铝合金焊接方法研究现状    4
1.3.1  熔化极脉冲MIG焊    4
1.3.2  MIG-TIG双面双弧焊接    4
1.3.3  激光—TIG双面焊焊接    5
1.3.4  等离子—TIG焊焊接    6
1.3.5  交流脉冲双面弧焊焊接    6
1.3.6  TIG双面对称焊接    6
1.4  螺旋管焊接    7
1.4.1  螺旋管带钢边缘铣削形状与焊接工艺的匹配    7
1.4.2  螺旋管焊接工艺参数与焊缝形貌的关系    8
1.5  课题主要研究内容    8
2  试验材料、设备及方法    10
2.1  双面双弧TIG 立焊试验方案设计    10
2.2  试验材料    11
2.3  试验方法    12
2.3.1  5083铝合金双面TIG焊接试验    12
2.3.2  金相分析试验    12
3  5083铝合金双面TIG焊接工艺试验研究    13
3.1  6mm5083试板焊接工艺参数    13
3.2  6mm5083铝合金焊接参数分析    14
3.2.1  电流变化的影响分析    14
3.2.2  枪间距变化的影响分析    15
3.2.3  弧长变化的影响分析    17
3.2.4  对接间隙的影响分析    18
3.3  焊缝射线检测    19
3.4  8mm和10mm5083铝合金焊接试验    19 铝合金螺旋管双丝焊接工艺技术研究:http://www.751com.cn/cailiao/lunwen_4240.html