摘要为了解决Al在304不锈钢脱氧过程中产生的脱氧产物对生产过程及产品质量的影响，通过研究Al-Si-Ca脱氧剂中组成成分等因素对脱氧效果的影响，从而获得Al-Si-Ca脱氧剂的成分范围，以便取代传统的Al脱氧。
实验结果表明：   （1）脱氧剂在1min至3min起效果。   （2）在Al含量差不多的条件下Ba和Si含量低的脱氧剂脱氧效果好。关键字： Al-Si-Ca-Ba；脱氧剂；脱氧效果6875
Abstract
In order to solve the problem about the effect of the deoxidation product of aluminum on the production process and the product quality for 304 stainless steel deoxidation, the effect of the composition in the deoxidant of Al-Si-Ca system on the result of deoxidization was investigated to get the good component of deoxidant and to replace the traditional Al deoxidation.
The experimental results show that:
   （1）Deoxidizer has the effect in 1min to 3 min.
   （2）The lower the content of the Ba and Si, the better the deoxidation, when the content of Al is the same.
KeyWords： Al-Si-Ca-Ba; deoxidizer, deoxidation effect
目录
1前言    1
1.1 脱氧剂的发展    1
1.1.1 硅脱氧    1
1.1.2 铝脱氧    1
1.1.3 钙脱氧    2
1.1.4 复合脱氧剂    3
1.2 钙系复合脱氧剂    3
1.3 Si-Ca-Ba复合脱氧剂    3
1.4 复合脱氧剂最佳成分的设计    5
1.5 选题的目的和意义    5
2 实验研究方法    7
2.1 脱氧剂主要元素及其成分范围的选择    7
2.2 试验设计方法    8
2.2.1 单纯型实验设计方法    8
2.2.2 约束条件    8
2.3 实验设备及材料    10
2.4脱氧剂的配置    14
2.5 实验过程    15
2.5.1 脱氧剂的制备    15
2.5.2 脱氧剂脱氧实验    16
3实验结果    17
3.1 所制备的脱氧剂成分    17
3.2 脱氧结果    17
4结果分析与讨论    19
4.1脱氧剂制备中各元素的收得率    19
4.2 脱氧剂的脱氧效果分析    20
5结论    22
致谢    23
参考文献    24
1前言
钢液脱氧是炼钢过程中必不可少的工艺环节，其中脱氧剂的选择至关重要。
脱氧是利用脱氧元素降低钢液氧含量的过程，包括与氧有强亲和力的脱氧元素和氧发生的脱氧反应及反应过程中产生的脱氧产物的上浮和排除。钢中氧含量的高低直接影响到最终钢材的质量和性能。高的氧含量会导致在钢液冷凝过程中，由于碳和氧偏析浓聚，将使碳再次发生氧化，使钢中产生气泡，而影响到钢材的质量;另外，氧还会以FeO、Fe304及其它氧化物形式析出，分布于晶界表面上，使钢的塑性、机械性能下降，并产生热脆、冷脆，对特殊用途钢的产品质量带来一系列的危害。
在1600℃的温度条件下，元素在钢中的含量为0.1%时，一些常见元素的脱氧能力由强到弱的排列顺序为：Re-Zr-Ti-B-C-P-Nb-V-Cr-W-Fe-Mo-Co-Ni-Cu。
有此可知，Mn、Si、Al、Ca是炼钢中常用的脱氧元素，在1600℃时他们的脱氧能力如表1所示：
表1  1600℃时Mn、Si、Al、Ca脱氧能力
脱氧元素（含量为1%）    Mn    Ca    Si    Al
钢液中平衡的w[O]%    0.10    0.00015    0.017    0.0017 Al-Si-Ca脱氧剂脱氧能力研究+实验分析:http://www.751com.cn/cailiao/lunwen_4622.html