摘要稀土永磁材料是支撑现代电子信息产业的重要基础材料之一，与人们的生活息息相关。小到手表、照相机、CD机、VCD机、计算机硬盘、光盘驱动器，大到汽车、发电机、医疗仪器等，永磁材料无所不在，然而稀土储量有限，无稀土永磁材料将引起极大重视并得到广泛应用。61955

本文研究的是以水热法为基础合成纳米级钴粉，通过改变时间和温度来观察钴粉的差异。其次，将纳米级钴粉和碳纳米管进行热处理制备ConC（CNTs），研究其磁性能的影响。最后，还研究了加入碳纳米管直接合成纳米级ConC粉体，通过调节温度等参量，研究其微观结构和磁性能的。

毕业论文关键词：水热法；纳米级钴粉；磁性能；碳纳米管；热处理

Abstract Rare earth permanent magnet materials is one of the support of modern electronic information industry an important base material,It is closely related to people's life.Small to watch,camera,CD player,VCD,computer hard drives,CD-ROM drives,big to cars,generators, medical equipment,etc..Permanent magnet materials are everywhere,However,rare earth reserves is limited, non-rare-earth permanent magnet materials will cause the great attention and widely used.

In this paper is based on hydrothermal synthesis of nanoscale cobalt powder,By changing the time and temperature to observe the difference of cobalt powder.Secondly,preparation ConC（CNTs）by the nanoscale cobalt powder and carbon nanotubes for heat-treating.To study the effect of the magnetic. Finally,Research the add carbon nanotube synthesis of nanoscale ConC powder directly. By adjusting the parameters such as temperature, to study the microstructure and magnetic. 

Key Words:hydrothermal method;nanometer cobalt;magnetic performance;carbon nanotubes;heat treatment 

1 绪论 1

1.1 引言 1

1.2 磁性材料分类 1

1.3 磁性材料基本特性 1

1.3.1 磁性材料的磁化曲线 1

1.3.2 磁性材料的常用磁性能参数 2

1.4 ConC化合物 3

1.5 ConC体系合成方法 4

1.5.1 电弧放电法 4

1.5.2 固相反应法 5

1.5.3 化学气相沉积法 5

1.5.4 爆轰合成法 6

1.5.5 水热法 6

1.6 研究意义及内容 7

1.6.1 研究的意义 7

1.6.2 研究的内容 8

2 实验部分 9

2.1 实验过程 9

2.1.1 实验原料 9

2.1.2 钴纳米线的制备工艺 9

2.1.3 水热法合成ConC粉体 10

2.1.4 热处理法合成ConC 11

2.2实验设备及仪器介绍 12

2.2.1 磁力搅拌器 12

2.2.2 真空干燥箱 13

2.2.3 反应釜（100mL） 14

2.2.4 X射线衍射仪(XRD) 15

2.2.5 扫描电子显微镜（SEM） 15

2.2.6 振动样品磁强计(VSM) 水热法合成无稀土永磁材料研究:http://www.751com.cn/cailiao/lunwen_67950.html