摘要本文综述了高氮钢，装甲钢的焊接研究现状和存在的问题，以及高能电子束焊接特点及运用优势，分析了高能电子束作为焊接热源时，高氮钢与装甲钢两种异种材料焊接的焊接性能，同时，分析了电子束焊接完成后对接接头宏微观组织，氮元素变化等特征，并研究了对接接头的典型缺陷，以及接头力学性能等。从而为此类材料研究以及电子束焊接加工工艺的过程制定提供参考。67694
毕业论文关键词 高氮钢 装甲钢 电子束焊接 焊接性
毕业设计说明书（论文）外文摘要
Title High nitrogen steel and dissimilar armor steel experimental study of electron beam welding
Abstract
This article reviews the research status of nitrogen steel and armor steel of EWB and existing problems, as well as high-energy electron beam welding characteristics and use of advantages, it is analyzed that the high energy electron beam welding as heat source,welding performance of two dissimilar kinds of high nitrogen steel and armored steel, mean while, analyzed its butt macro microstructure, general characteristics of the nitrogen distribution and researched typical defects of butt joints after electron beam welded, as well as joint mechanical properties. Thus it is provided that reference of such materials research and evolvement of electron beam welding process technology
Keywords nitrogen steel armor steel electron beam welding welding
目 次
1引言 1
1.1概述 1
1.2.1 高氮钢国内外焊接研究现状及存在的问题 2
1.2.2 装甲钢国内外焊接研究现状及存在的问题 3
1.2.3 高氮钢与装甲钢异种材料连接研究现状及存在的问题 4
1.3 电子束焊接研究 4
1.4 课题的目的和任务 6
2 实验设备，材料及方法 7
2.1 实验设备 7
2.1.1 焊接设备 7
2.2.2 试验测试与分析设备 7
2.2 实验材料 8
2.3 实验方法 8
3电子束焦点测量及焊接参数设定 10
3.1 电子束焦点测量 10
3.2 焊接参数设定 13
4异种材料母材及电子束接头宏微观组织特征分析 14
4.1.工艺参数与焊缝成形之间的关系研究 14
4.1.1 高氮钢与装甲钢表面堆焊成形分析 14
4.1.2 电子束束流参数与焊缝成形关系分析 15
4.1.3 电子束焦点位置与焊缝成形关系分析 17
4.2母材及焊缝微观组织特征分析 18
4.2.1 装甲钢及其融合区显微组织： 18
4.2.2 焊缝区 20
4.2.3 高氮钢及其融合区显微组织 21
4.3典型缺陷 22
4.3.1 气孔分析 高氮钢与装甲钢异种材料电子束焊接实验研究:http://www.751com.cn/cailiao/lunwen_75968.html