摘要Ti6Al4V具有优异的生物力学性能、耐腐蚀性以及生物相容性，但硬度低、耐磨性差，大大限制其在人工关节方面的应用。本实验以Na3PO4-Na2SiO3为电解液，在800Hz、占空比为20%时，对Ti6Al4V进行微弧氧化处理，通过调节电压和时间，研究微弧氧化对钛合金的润湿性能和摩擦学性能，以改善其生物相容性及生物摩擦学性能。测试氧化层的表面形貌、硬度；通过接触角实验评价经过微弧氧化处理的钛合金润湿性能，采用销-盘摩擦试验机研究改性Ti6Al4V在不同环境下的生物摩擦学性能。67812

毕业论文关键词： 微弧氧化   表面形貌   接触角   硬度    摩擦磨损

Title   Titanium alloy micro-arc oxidation ceramic membrane preparation and its performance research

Abstract

Ti6Al4V has excellent biomechanical performance, corrosion resistance and biocompatibility, but low hardness, poor wear resistance greatly limited its application in artificial joint. This experiment use micro-arc oxidation treatment on Ti6Al4V,use Na3PO4 - Na2SiO3 for electrolyte, at 800 Hz, 20% duty ratio , by adjusting the voltage and time, studied the micro-arc oxidation of titanium alloy wettability and friction resistance, in order to improve the biocompatibility and biological tribology performance. Tested the surface morphology, hardness of oxide layer; Evaluated the titanium alloy wettability by contact Angle experiments after micro-arc oxidation treatment ;use the pin - disk friction testing machine study modificatied Ti6Al4V biological tribology performance in different environment.

Keywords:  Micro-arc oxidation     surface topography     wettability   hardness    friction and wear

目录

一  引言 1

1.1  微弧氧化技术简介 1

1.1.1  微弧氧化技术 1

1.1.2  微弧氧化的基本机理概述及特点 1

1.1.3  微弧氧化的发展前景 2

1.2  钛合金的微弧氧化 3

1.2.1  我国医用钛合金的发展前景 3

1.2.2  钛合金微弧氧化概述 4

1.2.3  钛合金微弧氧化技术的现状及展望 5

1.3 本课题的研究内容 5

二  实验材料与方法 6

2.1  实验材料与设备 6

2.1.1 实验药品 6

2.1.2  实验设备 6

2.2  微弧氧化陶瓷膜的制备方法 7

2.2.1  钛合金表面处理 7

2.2.2  配制电解液 7

2.2.3  电参数的选择 7

2.2.4  实验过程 7

2.2.5  试样后处理 7

三 表面表征与性能测定 8

3.1  硬度 8

3.1.1  测定原理 8

3.1.2  测定步骤 9

3.2  接触角 10

3.2.1  测量原理 10