The purpose of this paper is to use waste fly ash, sand preparation of high performance fly ash aerated aerated silicate ceramsite, then, and made of ceramsite is a series of processing, to make ceramsite bibulous rate is low will greatly and ceramsite concrete strength, durability, etc can increased significantly. Preparation by prewetting haydite and learn how to deal with, hate water treatment and preparation of ceramsite concrete cladding processing and research on ceramsite and its concrete performance, can be economic, simple and reasonable production technology of high performance concrete.

Keywords Fly ash aerated silicate ceramic, prewetting treatment, cladding process, water-repellent treatment, ceramic concrete, water absorption

目   次

1  绪论 1

1.1  引言 1

1.2  轻集料混凝土的简介 2

1.3  陶粒 3

1.3.1  陶粒的性能 4

1.3.2  免烧陶粒的简介 4

1.3.3  陶粒预处理的研究现状 5

1.4  本课题的提出及主要研究内容 6

1.4.1  本课题的提出 6

1.4.2  本课题的主要研究内容 7

2  课题研究内容 7

2.1  轻质高强粉煤灰加气硅酸盐陶粒的制备 7

2.1.1  实验原料 7

2.1.2  主要仪器设备 8

2.1.3  陶粒的制备过程 9

2.1.4  陶粒的养护 10

2.2  陶粒的物理性能的测试 10

2.2.1  陶粒的堆积密度的测试 10

2.2.2  陶粒的筒压强度的测试 11

2.2.3  陶粒的表观密度的测试 11

2.2.4  陶粒的吸水率（1h，24h）的测试 12

2.4  制备轻集料混凝土 12

2.4.1  制备轻集料混凝土的原料 12

2.4.2  主要的仪器设备 13

2.4.3  混凝土的制备 13

2.4.4  混凝土的养护 14

2.5  混凝土试块抗压强度的测试 14

2.5.1  主要实验仪器 14

2.5.2  实验步骤 14

2.6  陶粒、混凝土试块的平行光双目体视显微观察 14

2.7  混凝土坍落度的测试 15

3  不同壳层结构的陶粒性能 15

3.1  不同壳层厚度的陶粒性能 15

3.2 不同壳层配比的陶粒性能 17

3.3 憎水处理的陶粒性能 19

3.4 陶粒密度 21

3.5  憎水处理陶粒的润湿角 21

4  不同壳层结构的陶粒混凝土性能 高性能超轻陶粒的制备与性能研究(2):http://www.751com.cn/cailiao/lunwen_76596.html