摘要介绍了钛合金的应用现状，钛合金的焊接性等特点。展开了一种TC4钛合金薄板的脉冲MIG焊方法的试验，采用OTC DP400MIG焊机，TC3材料焊丝进行焊接。期望可以解决传统TIG焊效率低成本高的问题。MIG焊能明显增大熔宽溶深，提高焊接速度，使工程效率得以提高。68197

在脉冲MIG焊接方法探索的起步阶段，本试验采用平面堆焊寻找可能的参数。 后系统地开展了TC4钛合金板材的对接试验，系统分析了焊接速度、焊接电流、焊接电压对焊缝成型的影响。并通过金相组织分析、微观硬度测试以及拉伸试验等对焊接接头的微观组织及力学性能做了分析。

毕业论文关键词：脉冲MIG焊  TC4钛合金  接头强度

毕业设计说明书（论文）外文摘要

Title  PMIG welding technology research of Titanium alloy sheet barrel and its pendant

Abstract

Applying condition of titanium alloy and its welding properties in introduced in this article. A experiment on PMIG welding of titanium is conducted. Aiming at substituding the common method, that is TIG welding in specific, of titanium welding. The PMIG welding is less costy and much more efficiency compared with TIG welding.

At the beginning of the experiment, we conduted surfacing test to find the best parameters of PMIG welding on Ti-6Al-4V alloy. After that a systematic research of butt joint and lap joint is conducted. In order to analysis the welding joint microstructure, micro-hardness test and tensile tests is done.

Keywords ：titanium alloy    PMIG welding    joint strength

目   次

1  引言 1

1.1  选题意义及背景 1

1.2  MIG焊技术的发展 1

1.2.1  国外MIG焊接技术发展现状 1

1.2.2  国内MIG焊接技术发展现状 2

1.2.3  MIG焊接技术的发展趋势 2

1.3  钛及其合金的焊接 3

1.3.1  纯钛的焊接 3

1.3.2  α钛合金的焊接 3

1.3.3  TC4的焊接 3

1.3.4  焊接钛合金使用的工艺 3

1.4  本课题主要研究内容 5

1.4.1  课题的具体内容 5

1.4.2  技术线路 5

2  PMIG焊接钛合金薄板的总体设计 6

2.1  PMIG焊接钛合金薄板计思路及技术难点 6

2.2  本章小结 6

3  PMIG焊接TC4薄板工艺试验 7

3.1  实验材料及条件 7

3.1.1  试验材料 7

3.1.2  试验设备 7

3.1.3  试验方法 9

3.2  脉冲MIG焊焊接钛合金薄板工艺试验 10

3.2.1  实验方案 10

3.2.2  坡口形式 10

3.2.3  焊前焊件的清理 10

3.2.4  焊丝材料 10

3.2.5　TC4钛合金脉冲MIG焊实验 钛合金薄壁筒体及挂件PMIG焊接工艺试验研究:http://www.751com.cn/cailiao/lunwen_76654.html