    摘要金属层状复合材料是由两层或两层以上不同性能的金属复合而成的。金属层状复合材料具有较高的强度、耐腐蚀性和良好的导电、导热等综合性能,因而在航天、化工、汽车以及日常生活用品等领域得到了广泛的应用。28249
    前期研究表明,本课题组提出的剧烈塑性变形方法:管状材料高压切变方法(t-HPS)有望用于双金属多层复合管的制备。根据t-HPS方法的切变特点,我们推断用该工艺制备双金属复合管材时,两种金属间的界面所占的比重会不断增大,我们称之为“界面倍增”现象。作为对这一猜想的初步实验研究,以纯铅和纯锡为模型材料加工双金属管,分别对样品进行不同旋转角度的t-HPS实验,并对得到的复合管进行了白光共聚焦分析,扫描电子显微镜分析,背散射电子衍射分析,显微文氏硬度实验,并分析了加工过程中的组织演变。研究结果表明界面达到良好的冶金结合,这种方法和累积轧制复合(ARB)工艺相比有显著差异,实验证明了t-HPS是一种可以用于制备双金属多层复合管的新方法。
    关键词  金属  层状复合材料  复合技术
    毕业论文设计说明书外文摘要
    Title  The Experimental study  of Laminated Bimetallic Composites Fabricated by Tube High-pressure Shearing with Interfaces Multiplication
    Abstract
    Laminated bimetallic composites(LMCs) is composed of two layers or more than two layers of different properties of the metal.LMCs has high strength,corrosion resistance,good electrical conductivity, thermal conductivity and other comprehensive performance. Therefore LMCs has been widely used in aerospace,chemical industry, automobile,daily necessities and other fields.
    Previous studies show that tube-high pressure shearing (t-HPS),a severe plastic deformation method proposed by our research group,is expected to be used for preparation of bimetallic multilayered composite tube. According to the shear characteristics of t-HPS method, we infer that during the preparation of bimetallic multilayered composite tube produced by the process, the ratio of the interface between the two kinds of metal will continue to increase, we call it "interfaces multiplication" phenomenon. As a preliminary experimental study on this conjecture, pure lead and pure tin are used for modeling material, the experiment is conducted with different angles of rotation. White light confocal analysis, scanning electron microscope analysis, back scattered electron diffraction analysis, micro Vickers hardness test are carried out for the composite tube, and the process of microstructure evolution is analysed. Research results show that good metallurgical bonding interface is reached, this method has significant differences compared with accumulative roll bonding (ARB) method, experiments prove that the t-HPS can be used for a new method for preparation of bimetallic multilayer composite tube.
    Keywords  metal  Laminated bimetallic composites(LMCs)  compostie technology
    目   次
    1  引言    1
    1.1本课题的研究意义    1
    1.2制备方法    1
    1.3管材高压切变原理    3
    1.4本文的研究内容    5
    2 实验材料与研究方法    6
    2.1 实验材料    6
    2.2 复合管的制备    6
    2.2.1 试验设备    6
    2.2.2 初始样品的制备    7
    2.2.3 复合管的制备过程    7
    2.3 分析测试方法    7
    2.3.1 金相组织观察    7
    2.3.2 白光共聚焦分析    8
    2.3.3 SEM 分析    8
    2.3.4 电子背散射衍射分析    8
    2.3.5 硬度分析    8
  1. 上一篇:高熔点材料复合热源搅拌摩擦焊接研究
  2. 下一篇:铝合金双面双TIG弧同步焊接试验研究
  1. 基于遗传算法与神经网络...

  2. 基于MATLAB的窄间隙焊缝质量建模研究

  3. 基于Ni基钎料的钼铼合金钎焊组织及性能研究

  4. 基于Mn-MOF的新型氧化锰/多...

  5. 高压动力锂电池正极材料...

  6. 基于铬酸锂的新型正极材...

  7. 基于锡纳米薄膜的灰度曝光研究

  8. 大众媒体对公共政策制定的影响

  9. 中考体育项目与体育教学合理结合的研究

  10. 十二层带中心支撑钢结构...

  11. 河岸冲刷和泥沙淤积的监测国内外研究现状

  12. 乳业同业并购式全产业链...

  13. 酸性水汽提装置总汽提塔设计+CAD图纸

  14. 当代大学生慈善意识研究+文献综述

  15. java+mysql车辆管理系统的设计+源代码

  16. 电站锅炉暖风器设计任务书

  17. 杂拟谷盗体内共生菌沃尔...

  

About

751论文网手机版...

主页:http://www.751com.cn

关闭返回