摘要本课题以乙烯基三甲氧基硅烷为单体，在碱催化下，水解缩合，制备出纳米乙烯基硅树脂。研究了水与单体的比例、反应时间等条件对硅树脂的影响。采用红外、XRD、TG等测试手段对其结构进行表征。结果表明：所制备的乙烯基硅树脂为纳米级，耐热性能优异。
- 上一篇：壁纸水性油墨的研制+文献综述
- 下一篇：GCr15轴承钢热处理后相结构和尺寸变化研究
采用巯基乙酸通过点击化学方法对纳米乙烯基硅树脂进行改性。通过红外、TG、分散性实验对点击产物进行表征，结果表明乙烯基硅树脂和巯基乙酸反应制备出巯基乙酸改性的乙烯基硅树脂。6016
关键词 点击化学 乙烯基硅树脂 巯基烯反应 表面修饰
毕业设计说明书（论文）外文摘要
TitleStudy on modification of nanoparticles by click chemistry
Abstract
In this paper, the nano vinyl silicone resin（NVSR）particles were synthesized by vinyltrimethoxysilane with basic as catalyst. The water /monomers ratio, reaction time and other conditions on the effect of silicon resin preparation were investigated. The structure and performance of NVSR was confirmed by FT-IR spectroscopes, X-ray diffraction (XRD) and thermogravimetric analysis (TGA). The results show that the prepared vinyl silicone resin particles were nanometer grade and with excellent heat resistance.
The vinyl silicone resin particles were modified using mercaptoacetic acid via click chemistry method. By FT-IR, TGA, dispersion experiment on click product, the results show that the mercaptoacetic acid wassuccessfully grafted on vinyl silicone resin.
Keywords click chemistry vinyl silicone resin thiol-ene reaction surface modification
目 次
1 引言 1
1.1 点击化学 1
1.1.1点击反应的类型 1
1.2点击化学的研究进展 3
1.2.1点击化学在制备树枝状分子中的研究 3
1.2.2点击化学在生物大分子合成中的研究 3
1.2.3点击化学在医药及材料中的研究 4
1.2.4点击化学在纳米粒子中的研究 5
1.2.5点击化学在表面修饰中的研究 5
1.2.6点击化学在在高分子中的研究 6
1.2.7自由基引发的巯基-烯反应的研究 7
1.2.8点击化学在在其它领域中的研究 7
1.3 本课题的主要研究工作 7
2 纳米乙烯基硅树脂的制备 9
2.1 概述 9
2.2 实验部分 9
2.2.1实验原料与仪器 9
2.3 乙烯基硅树脂的制备 10
2.3.1性能测试 11
2.4 结果与讨论 11
2.4.1单体与水之比对产率的影响 11
2.4.2 XRD分析 12
2.4.3红外光谱分析 13
2.4.4透射电镜分析 14
2.4.5耐热性能分析 15
3点击化学方法对乙烯基硅树脂修饰 17
3.1概述 17
3.2实验部分 17
3.2.1实验原料与仪器 17
3.2.2纳米乙烯基硅树脂微球的表面修饰 18
3.2.3性能测试 18
3.3结果与讨论 19
3.3.1 点击化学机理 19
3.3.2耐热性能分析 19
3.3.3 红外分析 20
3.3.4 分散性分析 21
3.3.5 沉降分析 22
结论 23
致谢 24
参考文献 25
1 引言