摘要：本论文从成核剂的作用机理出发，介绍了不同用量的成核剂对玻纤增强尼龙66结晶和力学性能的影响。利用双螺杆挤出造粒机组制备出了性能优异的玻璃纤文增强尼龙66工程塑料。
- 上一篇：纳米稀土改性聚氨酯弹性体的研究+文献综述
- 下一篇：B2级PU外保温材料配方研究+文献综述
结果表明，成核剂的加入使玻纤增强尼龙66结晶速率提高，结晶温度提高；随着成核剂的加入玻纤增强的力学性能均增强，弯曲强度、弯曲模量、断裂强度和冲击强度均有所增加，耐热性无明显变化，断裂伸长率降低。6207
关键词： 玻纤增强；成核剂；结晶；力学性能；尼龙66
Influence of nucleating agent on the crystallization of glass fiber reinforced nylon 66 crystallization and mechanical properties
Abstract: In this paper, the content of nucleating agent on the glass fiber reinforced nylon 66 crystallization effects and mechanical properties are introduced by the mechanism of nucleation agent. The high performance glass fiber reinforced nylon 66 engineering plastics were prepared by the twin-screw extrusion granulation unit.
The results show that the addition of nucleating agent make the crystallization rate of the glass fiber reinforced nylon 66 crystallization rate increase and the crystallization temperature increases. With the addition of nucleating agent mechanical properties of glass fiber reinforced increase, the flexural strength, flexural modulus, tensile strength and impact strength are increased, heat resistance did not change significantly, the elongation at break decreased.
Key Words: glass fiber reinforced；nucleating agent；crystallization；mechanical property；nylon 66
目录
摘要 i
Abstract i
目录 ii
1 文献综述 1
1.1 选题的背景与意义 1
1.2 玻璃纤文 2
1.2.1 玻璃纤文的组成纤文的组成及其作用 2
1.2.2 玻璃纤文的性能 2
1.2.3 玻璃纤文的分类 3
1.3 尼龙66玻纤增强改性研究发展 3
1.3.1 玻纤增强的机理 4
1.3.2 玻纤增强的国内外进展 4
1.3.3 玻纤增强的缺点 5
1.4 成核剂 5
1.4.1 成核剂的特征 5
1.4.2 成核剂的种类 5
1.4.3 成核剂的作用 6
1.4.4 成核剂活性的测定 7
1.4.5 成核剂的机理 7
2 实验部分 9
2.1 实验原材料和药品 9
2.2 实验用仪器设备 9
2.3 试样制备 9
2.3.1 共混 9
2.3.2 干燥 10
2.3.3 挤出 10
2.3.4 注塑 10
2.4 测试与表征 11
2.4.1 拉伸性能测试 11
2.4.2 弯曲性能测试 11
2.4.3 缺口冲击(J/m)测试 11
2.4.4 悬臂梁冲击(J/m)测试 11
2.4.5 热变形温度测试（HDT） 12
2.4.6 DSC测试 12
3 结果与讨论 13