摘要本课题论文利用国韵WH系列高频感应加热电源，采用黄铜钎料、铜磷钎料对T2纯铜高频感应钎焊，实现铜-铜同种金属钎焊的试验中表现出良好的焊接性。 通过感应钎焊工艺试验，得出了黄铜钎料钎焊T2纯铜的最佳焊接温度为950°C；铜磷钎料钎焊T2纯铜的最佳焊接温度为700°C。经力学性能检测，黄铜钎料钎焊T2纯铜的剪切强度为175MPa，脆性断裂；铜磷钎料钎焊T2纯铜的剪切强度为202MPa，塑性断裂。金相试验表明，黄铜钎料的钎层组织为Cu-Zn合金，为α+β相；铜磷钎料的钎层组织为Cu-P合金，为α+β相。7272
- 上一篇：SiC浆料性能与多孔陶瓷烧结研究+文献综述
- 下一篇：铜复合热源搅拌摩擦焊接工艺研究
关键词 感应钎焊，T2，黄铜钎料，铜磷钎料，剪切强度，金相组织
毕业设计说明书（论文）外文摘要
Title Experimental study of the induction brazing of copper
Abstract
The subject of the use of the country rhyme WH series of high-frequency induction heating power supply, brass brazing copper-phosphorus brazing T2 copper high-frequency induction brazing welding，achieve of copper - copper metal brazing trials showed good weldability. Obtained through the induction brazing process test brass brazing T2 copper best soldering temperature of 950 ° C; copper-phosphorus brazing T2 copper soldering temperature of 700 °C. Mechanical properties testing, brass brazing T2 pure copper shear strength of 175MPa, the brittle fracture; T2 copper, copper-phosphorus brazing filler metal shear strength of 202MPa, the ductile fracture. Metallographic tests showed that the brass brazing filler metal organization for the Cu-Zn alloy, for α + β phase; the organization of the copper-phosphorus brazing filler metal Cu-P alloy, for α + β phase.
Keywords induction brazing, T2, brass brazing，copper-phosphorus brazing, shear strength, microstructure
目 次
1.引言 1
1.1研究意义 1
1.2 研究现状 1
1.2.1 感应钎焊 2
1.2.2 铜的焊接 3
1.2.3 钎料 4
1.3 本课题的研究内容简介及任务 5
2 实验设备及实验材料 6
2.1 实验设备 6
2.1.1 感应加热电源 6
2.1.2 感应线圈 7
2.1.3 金相显微镜及计算机处理系统 7
2.1.4 金相试样水磨机 8
2.1.5 显微硬度计 8
2.2 实验材料 9
2.3 钎料 9
2.4 钎剂 10
3 感应钎焊铜实验 11
3.1 感应钎焊原理 11
3.2 电磁感应加热特点 12
3.3 焊接前准备 12
3.4 感应钎焊实验 13
3.5 焊接工艺 14
4 金相实验 15
4.1金相实验方法概述 15
4.2 制样 16
4.3 金相分析 17
4.3.1 宏观图 17
4.3.2母材 18
4.3.3焊缝 19
4.3.4熔合线 20
4.3.5钎料 22
5 力学性能 23
5.1 硬度测试 23
5.2 剪切强度测试 24
6 分析讨论 25
6.1 感应钎焊缺陷讨论 25
6.2 不同钎料对焊接性能影响的对比分析 27
6.3 改善感应钎焊接头质量方法的讨论 27
结 论 28