    (Standards Australia 2009), GB50010-2010 (China Building In-
    dustry Press 2010), ACI 318-05 (American Concrete Institute
    2005), and Eurocode 2 [European Committee for Standardization
    (CEN) 2004]) contain a variety of formulas for calculating the com-
    pression development lengths. The majority of the experimental
    data from which most of these formulas have been developed have
    been obtained using lower strength bars.
    This paper reports further research in this field. Through a
    series of pushout experiments, the compressive bond properties of
    500 MPa reinforcing bars in concrete are studied.
    Like the tensile anchorage properties of the bar, the factors
    influencing bond under compressive conditions can be classified
    into four main groups:
    1. Influence of concrete on bond: concrete compressive strength,
    concrete tensile strength, concrete cover, grading of aggregate,
    consistency of fresh concrete, and fibers in concrete.
    2. Influence of position of bar on bond: position of bar during
    casting, position of bar relative to the nearest flexural crack,
    and width of splitting crack along the bar.
    3. Influence of reinforcement on bond: relative rib area of bar,
    rib pattern of bar (including inclination and shape of ribs),
    diameter of bar, coating (epoxy coating for steel bars or sandcoating for nonmetallic bars), corrosion of steel bars, amount
    of transverse reinforcement, stress in the reinforcement, and
    bar spacing.
    4. Influence of load on bond: transverse pressure in anchorage
    area, monotonically increasing loading (including influence of
    loading rate), long-term loading, cyclic, loading and reversed
    cyclic loading.
    The final bond strength is also dependent on the embedded
    length. All of these parameters influence compressive bond behav-
    ior in different ways. In specific cases, careful analysis is required.
    However, for any given type of the reinforcing bars and type of
    concrete, five of these factors have been found to have significant
    influence on the bond strength (Mao et al. 2004; Xu et al. 1994).
    This paper addresses the influence of each of these fivemain factors
    (strength of the concrete, size of the bar, concrete cover, embedded
    length, and transverse reinforcement) on the compressive bond
    strength of 500 MPa reinforcing bars. A program of pushout tests
    designed to evaluate the influence of each of these factors sepa-
    rately is reported. Based on the results, a formula for bond strength
    taking into account these factors is proposed.
    Experimental Program
    The experimental program reported in this paper involved a series
    of 99 pushout tests. In each test a length of reinforcing bar was
    cast into a cylinder of concrete and then pushed out by a testing
    machine. Each cylinder was supported so as to ensure the bar could
    be pushed out of the cylinder without interference. Parameters were
    varied to determine the influence of strength of the concrete, size of
    the bar, concrete cover, embedded length, and transverse reinforce-
    ment on the compressive bond strength of 500 MPa reinforcing
    bars. The concrete mixes were typical of normal strength Chinese
    construction concrete. All the concrete components including
    the cement, water, sand, and aggregate were identical, while the
    proportions were varied to achieve the various concrete strengths.
    The effect of admixtures was not investigated. For each combina-
    tion of parameters, three tests were performed.
    The reinforcement bars (Li et al. 2010) used all had nominal
    yield strength of 500 MPa and the rib pattern shown in Fig. 1.
    The bars were embedded in cylinders of concrete with diameters
    of 100 or 150 mm, with a single deformed bar in each cylinder.
    The bar position was determined by the minimum value of the
  1. 上一篇:公路桥梁英文文献和中文翻译
  2. 下一篇:精密控制的高速注塑机英文文献和中文翻译
  1. 变频器在供水控制系统的...

  2. 柴油机连杆英文文献和中文翻译

  3. 传感元件英文文献和中文翻译

  4. FD生成的PMM数据在初步设计...

  5. 加固纤维聚合物增强混凝...

  6. 非线性循环行为混杂纤维...

  7. 在平衡的轴向荷载下K型管...

  8. java+mysql车辆管理系统的设计+源代码

  9. 中考体育项目与体育教学合理结合的研究

  10. 杂拟谷盗体内共生菌沃尔...

  11. 当代大学生慈善意识研究+文献综述

  12. 酸性水汽提装置总汽提塔设计+CAD图纸

  13. 河岸冲刷和泥沙淤积的监测国内外研究现状

  14. 大众媒体对公共政策制定的影响

  15. 乳业同业并购式全产业链...

  16. 十二层带中心支撑钢结构...

  17. 电站锅炉暖风器设计任务书

  

About

751论文网手机版...

主页:http://www.751com.cn

关闭返回