摘要：氟化石墨烯作为石墨烯的新型衍生物，由氟化石墨经一系列反应剥离而成，由于氟原子的插入，相比石墨烯具有更好的物理化学性能。本课题是通过化学剥离法对氟化石墨进行剥离制备氟化石墨烯，并且研究了剥离试剂及剥离条件对剥离效果的影响，进一步再利用拉曼、X射线衍射、扫描电镜对剥离产物进行了表征。研究结果表明：氟化石墨在NMP中超声处理虽然能够剥离，但是也有一定的缺陷，耗时长，效率低。而在HClO4中剥离，效果较好。反应4小时的层间距最大，剥离效果最好；反应时间越长，氟化石墨烯结构的规整度越低；反应4小时的片层结构最清晰。21635
- 上一篇：年产800吨多聚磺酸-聚苯乙烯嵌段共聚物的合成工艺设计
- 下一篇：钕铁硼镀双层镍工艺分析
毕业论文关键词：氟化石墨；剥离；氟化石墨烯；超声
Detachment of graphite fluoride
Abstract: Graphite fluoride as graphene's new derivatives, stripping by graphite fluoride through a series of reaction, and because of the introduction of fluorine atoms, compared to graphene has better physical and chemical properties. This topic is through chemical stripping stripping of graphite fluoride preparation of graphite fluoride, and studied its reagent and the effects of the conditions on the stripping further using Raman and X-ray diffraction (XRD), scanning electron microscopy (sem) for stripping the product have been characterized. The results show that graphite fluoride ultrasonic processing in NMP can peel, but there's also some shortcomings, like time-consuming and inefficient. In the HClO4 stripping, the effect is better.The layer spacing of 4 hours’ reaction time is the biggest, stripping effect is best; The longer the reaction time, the structure of graphite fluoride ene neat degree is lower;The film layer structure of 4 hours’ reaction time is clearest.
KeyWords：Graphite fluoride; Stripping; Graphite fluoride; ultrasonic
目录
1 绪论 1
1.1 研究的背景与意义 1
1.1.1 研究的背景 1
1.1.2 研究的意义 1
1.2 氟化石墨的性质与应用 2
1.2.1 氟化石墨的性质 2
1.2.2 氟化石墨的应用 2
1.3 石墨烯的性质与应用 3
1.3.1 石墨烯的性质 3
1.3.2 石墨烯的应用 4
1.4 氟化石墨的制备方法 5
1.4.1 气相法 5
1.4.2 固相法 5
1.4.3 电解合成法 6
1.5 石墨烯的制备方法 6
1.5.1 微机械剥离法 6
1.5.2 取向附生法 6
1.5.3 外延生长法 7
1.5.4 氧化石墨还原法 7
1.5.5 化学插层法 8
1.5.6 化学气相沉积法 8
1.5.7 碳纳米管轴向切割法 9
1.6 氟化石墨烯的制备方法 9
1.6.1 固相法 9
1.6.2 液相法 10
1.6.3 气相法 10
1.6.4 剥离法 10
1.7 本课题研究内容 11
2 实验部分 12
2.1 实验药品 12
2.2 实验仪器 12
2.3 实验步骤 12
2.4 样品的表征 13
3 结果与讨论 15
3.1 在NMP中剥离 15
3.1.1 XRD表征与分析 15
3.2 在HClO4中剥离 16
3.2.1 XRD表征与分析 16
3.2.3 扫描电镜分析 20