摘要：目前报道的介孔二氧化钛孔体积比较小、晶体结晶度不高，从而影响了催化性能。而我们用表面活性剂F127为模板剂、钛酸四正丁酯为钛源、正硅酸四乙酯（TEOS）和酚醛树脂（Resol）作为无机和有机前驱体，用蒸发诱导自主装的方法合成出大比表面积、高结晶度的介孔二氧化钛。以此为载体负载金纳米粒子，并用于CO催化氧化，当金纳米粒子的含量为0.5-1.0wt%时，催化剂在较低的反应温度下就能达到100%的转化率。22456
- 上一篇：含柠檬酸络合剂的酸性化学镀镍液使用周期研究
- 下一篇：苯基乙烯基硅树脂的制备及其应用
毕业论文关键词：介孔二氧化钛，合成，CO催化氧化
Controllable Preparation of mesoporous titania and study the performance of catalytic oxidation of carbon monoxide
Abstract：It is currently reported that mesoporous titania pore volume is relatively small, the crysta lis not high crystallinity, thus affecting the catalytic performance.We use F127 surfactant as the template, tetra-n-butyl ester as a titanium source, tetraethylorthosilicate (TEOS) and phenolic resin (Resol) as inorganic and organic precursors, induced by the evaporation method for the synthesis of independent loaded the specific surface area, high crystallinity of mesoporous titania. As a carrier-supported gold particles and for CO oxidation, when the content of gold particles is 0.5-1.0wt%, the catalyst at a lower reaction temperature can reach100%conversion.
Keywords: mesoporous titania, synthesis, the catalytic oxidation of CO
目录
1 绪论 4
1.1 研究背景 4
1.1.1 介孔材料 4
1.1.2 二氧化钛的结构与性质 5
1.1.3介孔二氧化钛材料的合成方法 5
1.2一氧化碳 6
1.2.1 一氧化碳的基本性质 6
1.2.2 一氧化碳低温氧化性能催化剂 6
1.2.3 一氧化碳低温催化氧化机理 7
1.2.4 CO氧化催化剂的制备方法 7
1.2.5环境气氛对CO催化氧化的影响 8
1.3.应用前景 9
1.3.1 二氧化钛的应用前景 9
1.3.2 一氧化碳的应用前景 10
1.4 本课题研究的目的和意义 11
2 实验部分 12
2.1 仪器与试剂 12
2.1.1 实验试剂 12
2.1.2 实验仪器 12
2.2 介孔二氧化钛的制备 13
2.2.1实验步骤 13
2.2.2 介孔二氧化钛的表征方法 13
2.2.3 制备介孔二氧化钛 13
2.3 一氧化碳催化活性实验 25
3 结果与讨论 26
3.1 最佳介孔二氧化钛的结果分析 26
3.1.1 XRD分析 26
3.1.2 能谱图分析 39
3.1.3 N2吸附-脱附图分析 39
3.2 一氧化碳催化活性实验分析 40
4 结论 42
致谢 43
参考文献 44
1 绪论
1.1 研究背景
美国某石油公司在1992年通过以表面活性剂为模板，制备出了介孔材料。 这种介孔材料的诞生将从介孔分子微孔介孔分子筛的开发领域的规则，沸石分子筛上完成在催化，吸附分离过程表现出广阔的应用前景。从那个时候开始，介孔材料的研究制备话题变得越来越重要与常见。目前二氧化钛介孔材料的研究越来越受到大家的关注[1]。所以我们应该要对二氧化钛介孔材料进行不断的探讨和研究。
一氧化碳是一种典型的有毒化合物，是催化氧化反应的研究中常用的物质，但也监测和消除最直接的，最便宜的方式成为环境科学，材料科学和有效的，分析科学研究的重点领域。