    摘要FOX-7是一种新型高能钝感含能材料,其优异的综合性能引起世界各国的广泛关注。激光起爆技术是具有高安全性和高可靠性的新型起爆技术。本文针对FOX-7的激光直接起爆与激光驱动飞片起爆技术开展了初步的探索性研究。33376
    分析了纯FOX-7、2%碳纳米管/FOX-7、5%碳纳米管/FOX-7以及10%碳纳米管/FOX-7的微观形貌,测试了纯FOX-7、2%碳纳米管/FOX-7、5%碳纳米管/FOX-7以及10%碳纳米管/FOX-7的激光吸收性能。随着FOX-7炸药中碳纳米管掺杂量的增加,碳纳米管在FOX-7炸药颗粒上的分布愈发均匀;未掺杂碳纳米管的FOX-7的激光吸收性能极差,几乎将照射到药剂表面的激光完全反射;在FOX-7中掺杂碳纳米管有效提高了其对激光的吸收率。然而,在目前的实验条件下,采用自由振荡激光与调Q激光均未能将FOX-7成功起爆。
    研究并分析了装药压药密度分别为2.399g/cm3、2.256 g/cm3、2.212 g/cm3以及2.002 g/cm3条件下FOX-7炸药的激光驱动飞片起爆情况。虽然激光成功地驱动了飞片,但是FOX-7并未被成功起爆。
    关键词:FOX-7,激光起爆,激光驱动飞片,碳纳米管
    毕业论文设计说明书外文摘要
    Title   Experimental study on the initiation of FOX-7 laster
    Abstract:
    FOX-7 is a new energy insensitive energetic material, and its excellent comprehensive performance has caused wide attention in the world.. Laser initiating technology is a new initiating technology with high security and high reliability.. In this paper, the preliminary exploratory research on the laser direct detonation and the laser driven flyer initiation technology of FOX-7 is carried out.
    The pure FOX-7, 2% carbon nanotubes /FOX-7, 5% carbon nanotubes /FOX-7 and 10% carbon nanotubes /FOX-7 micro morphology analysis tested pure FOX-7, 2% carbon nanotubes /FOX-7, 5% carbon nanotubes /FOX-7 and 10% carbon nanotubes /FOX-7 laser absorption performance of. With increase of FOX-7 explosives in carbon nanotubes doped, carbon nanotubes in explosive FOX-7 particle distribution increasingly uniform; not doped carbon nanotubes FOX-7 laser absorption performance is poor, almost perfectly reflecting surface chemical laser irradiation; FOX-7 doped carbon nanotubes can effectively improve the rate of the absorption of the laser. However, in the present experimental conditions, the FOX-7 laser and the Q laser can not be successfully initiated by the free oscillating laser and the laser.
    The density of the explosive charge was studied and analyzed, and the laser driven flyer detonation of the FOX-7 explosive was 2.399g/cm3, 2.256 g/cm3, 2.212 g/cm3 and 2.002 g/cm3 respectively.. Although the laser successfully drives the flyer, the FOX-7 has not been successfully initiated.
    Keywords: FOX-7, laser initiation, laser driven flyer, carbon nanotube
    目   次
    1 绪论    1
    1.1 激光起爆技术概述    1
    1.2 激光起爆炸药的机理    3
    1.3 本文研究内容    4
    2 FOX-7的形貌与性能分析    5
    2.1 FOX-7的表面形貌分析    5
    2.1.1 FOX-7的宏观形貌    5
    2.1.2 FOX-7的微观形貌    6
    2.2 F0X-7的爆炸性能分析    11
    2.3 FOX-7的光学性能分析    11
    2.4 小结    15
    3 激光起爆FOX-7的实验研究    17
    3.1 实验装置与方法    17
    3.1.1 实验仪器介绍    17
    3.1.2 激光的稳定性    18
    3.1.3 激光的光束特性    18
    3.1.4 激光起爆FOX-7炸药的实验方法    19
    3.2 实验结果与分析    21
    3.2.1 实验结果    21
    3.2.2 实验分析    22
    3.3 小结    22
  1. 上一篇:氮掺杂石墨烯改性电极在生物电化学体系中的应用研究
  2. 下一篇:二维硫化镍基复合材料的制备及其性能研究
  1. 基于非对称六羧基配体的...

  2. 管线钢X80在氯离子环境中...

  3. 钯催化下咪唑并[1',2'1,5]吡...

  4. 含脲基的金属-有机框架材...

  5. 有机物反磁磁化率的拓扑研究

  6. 纳米Trögersbase衍生物催化...

  7. 有机物标准熵的拓扑研究

  8. 当代大学生慈善意识研究+文献综述

  9. 十二层带中心支撑钢结构...

  10. 大众媒体对公共政策制定的影响

  11. 酸性水汽提装置总汽提塔设计+CAD图纸

  12. 乳业同业并购式全产业链...

  13. java+mysql车辆管理系统的设计+源代码

  14. 河岸冲刷和泥沙淤积的监测国内外研究现状

  15. 中考体育项目与体育教学合理结合的研究

  16. 电站锅炉暖风器设计任务书

  17. 杂拟谷盗体内共生菌沃尔...

  

About

751论文网手机版...

主页:http://www.751com.cn

关闭返回