摘要聚乳酸( Polylactic Acid)是一种具有良好生物相容性和降解性的聚合物材料,可极好的适用于生物医学领域。且多孔无纺布材料由于其可自支撑、高比表面积及具有可控孔结构的特点受到广泛的关注。本文采用静电纺丝法和溶液共混法制备聚乳酸多孔纤维。即用氯仿作共溶剂混合聚乳酸和聚环氧乙烷,电纺出该二元组份的纳米纤维,后使用蒸馏水刻蚀聚环氧乙烷相,最终获得多孔聚乳酸无纺布,并通过调控电纺溶液的浓度及两组分的比例来改变纤维的形貌和多孔结构。47365
毕业论文关键词:静电纺丝 原理 纳米纤维 粘度 多孔材料
Abstract: Polylactic acid (Polylactic Acid) is a biocompatible and biodegradable polymeric materials which can be applied to an excellent biomedical field.And a porous non-woven material may be self-supporting because of their high specific surface area and pore structure characteristics with controlled attracted much attention.In this paper, electrospinning method and solution blending Preparation of porous PLA fibers.The mix up polylactic acid and polyethylene oxide with trichloromethane as co-solvent.Electric spinning component of the tuple nanofibers,and then polyethylene oxide phase were etched by distilled water.Finally obtained porous polylactic acid nonwoven fabric, to alter the morphology and porous structure of the fiber which to control by spinning solution concentration and the ratio of the two components.
Keywords: electrospinning nanofibers principle viscosity porous material
目 录
1、绪 言4
1.1、静电纺丝来源与发展-4
1.2、PLLA优点与应用--4
1.3、PEO优点与应用以及制备方法5
1.4、无纺布及其应用--5
1.5、静电纺丝法制备多孔PLLA无纺布--6
1.6、高分子合金6
1.7、实验原理--7
2、实验部分9
2.1、 实验药品和仪器:--9
2.1.1、药品--9
2.1.2、仪器--9
2.2、实验过程--9
3、实验数据处理和结论--11
4、实验展望16
5、参考文献17
致谢--19
1、绪言:
1.1、静电纺丝来源与发展
“静电纺丝”一词来源于“electrospinning【1】”,比这个更加早一些的就是“electrostatic spinning”,而我们国家一般简称为“静电纺”、“电纺”等。而静电纺丝就是高分子流体静电力雾化下的特殊形式,其起源一般追溯到1934年Formalas制造出用静电力制备聚合物纤维的实验装置,后来申请到专利,这一项成果也逐渐被世人公认为静电纺丝技术制备纤维的开端。90年代以后得到了发展,并且随着纳米材料广泛应用,又产生出了纳米纤维。静电纺丝也越来越多的被用到各个更加重要的领域,比如光催化【2】,,生物科学等等,在静电纺丝的过程中对于电场的理解也是各不相同【3】,一般用的静电压在0-70KV之间。
对于现在的静电纺丝技术已经是制备纳米材料领域里面最为重要的的学术与技术,由于其制造装置简单,加工方便,并且可以纺丝的种类很多等等优点成为现在很多科学家深入研究的基石。尽管静电纺丝技术的优点很多,但是还是有尚要解决的问题摆在我们的面前,比如制备有机纳米纤维方面,天然高分子的种类还是很少,原料的种类少的结果就会影响人们对产品的结构和性能等等研究就会不深入。另外还有静电纺丝技术对于无机纳米纤维的研究还是处于起始阶段,对于无机纳米纤维在高物过滤、催化、航天等材料的研发发展比较慢。