力能参数用VB程序编程，计算校核，成品率为80.1%为合格。
综上所述，本课题中压电缆用紫铜带产品的性能及其工艺设计符合现代工艺，满足现实工厂实际情况，计算无不合格。
毕业论文关键词：中压电缆；无氧铜TU2；工艺制度；力能参数
Medium voltage cable with copper belt performance of product and process design
General Description of the Design: The design is conducted on the basis of medium-pressure cable which utilizes the products’ characteristics from red copper.It is calculated and researched in the way of practical survey such as Chinalo Shanghai copper co.,LTD.also, I have consulted with some engineers guiding me to observe the equipments of the factory, which have done a great help to look into the concrete inner materials in the company.
The medium-pressure cables dominantly focus on cables which are 35KV below. Used in the manufacture of cable are mainly copper and aluminum cable,and the purpose of this design USES copper cable and the reason is:1. Low resistivity. 2. Good ductility: extending rate of 20 to 40% of the copper alloy. 3. High strength.4. The antifatigue: Aluminum repeated bending rupture easily, copper is not easy. Elastic indicators, copper is about 1.7 ~ 1.7 times higher than aluminum.5. Good stability and corrosion resistance: copper oxidation and corrosion resistance. Due to the above differences in physical properties, on the application, copper core cable has more advantages than al core cable: 1. Carrying capacity is big.2. Low voltage loss.3. Low heating temperature: in the same electrical flow, with the cross section of copper core of calorific value is smaller than the aluminum core cable, makes the operation more safety.4.Low energy consumption: due to the low resistivity of copper, al cable compared to copper cable power loss is low, it is obvious. This is helpful to improve the utilization rate of power generation and protect the environment.5. Oxidation resistance, corrosion resistance, copper core cable connector performance is stable, not an accident due to oxidation.6. Construction is convenient. Therefore, copper cable in the cable power supply, especially in underground cable power supply areas, has outstanding advantages.
This design according to the product USES the research method is the TU2 copper. Standard: （GB/T 5231-2001) ,the advantage of oxygen and low impurity content, high purity, conductive, thermal conductivity, excellent, good ductility, hydrogen permeability rate is low, no "disease" or rarely hydrogen "disease"; Processing performance and corrosion resistance of welding, cold resistance are good. Size of raw material is 170mm×630mm×5100mm, the finished product size is 0.6mm×600mm×1000mm, volume weight 3.204kg. Delivery status to hard mode. The main technological process of this design TU2: by copper melting furnace heating with water after holding furnace heat preservation and the analysis of the composition adjustment, enter the semi-continuous casting machine casting, cast ingot billet, after cutting, saying machine into heating, hot rolling process, wait for after cooling of the milling surface to remove surface oxide layer looped machine rolls, then entered the stage of cold rolling, after cutting head to tail, the use of bell type annealing furnace for annealing in the middle. After the fire product under normal pressure and able to enter the finishing mill under further pressure heat treatment of finished products and then USES the air cushion type annealing furnace. When, after the completion of the whole annealing for final shear straightening, product quality inspection, confirm the product conform to the requirements of the delivery can packaging warehousing, waiting for the delivery of the goods. Product technical requirements can be summarized as: precise dimension good flatness, smooth surface, high performance products in order to achieve the basic premise of technical requirements for the design. The selection of the equipment in the design of the main reference for the production of aluminum used equipment, reversing two roll mill, four high cold rolling mill, twelve roll finishing mill, the bell type annealing furnace and so on. Clear understanding of the calculation process of rolling force and rolling moment will formulate the reasonable VB language, and the use of CAD map roll, roll force and bending torque diagram and the plant layout, main equipment strength and motor ability check parts before learning the teaching material content is calculated to verify. The principle of this design is under the premise that guarantee the quality of design products, as far as possible, reduce production cost, improve production efficiency. This design mainly elaborated the TU2 production technical requirements and key production processes (melting, casting, milling, rolling, annealing, etc.) of the process characteristics. According to Chinalco Shanghai copper co., LTD., the existing production process and product, the product production making, rolling system of the melting process, roller type system formulation, motor ability, roll strength, respectively, in the design process using computer software, Visual Basic programming language for the rolling force and rolling torque calculation program compiled, using computer Auto CAD software, to draw roll figure. To design products that meet the actual production standards and its production process. 中压电缆用紫铜带产品的性能及其工艺设计(2):http://www.751com.cn/cailiao/lunwen_35430.html