ZnO/C陶瓷植物叶片模板的超疏水陶瓷的制备及性能研究

摘要近年来，由于仿生超疏水性表面在自清洁、防腐蚀、微流体系统和生物相容性等方面所显示的独特性能以及在国防、工农业生产和日常生活中的潜在应用前景，有关超疏水表面的研究引起了科研工作者的极大关注。而直接利用自然界丰富的、经过长期进化而成的、具有特殊结构和功能的生物模板来制备具有生物结构的无机新材料，是材料制备的一个新思路、新概念。本研究以荷叶和粽叶为模板，通过浸渍、烧结等步骤，制备了ZnO/C陶瓷，并分析了其表面形貌、成分组成以及疏水性能。制备的ZnO/C陶瓷接触角超过150°，具有很好的超疏水性。67235

毕业论文关键词：超疏水氧化锌

毕业设计说明书（论文）外文摘要

Title Preparation and hydrophobicity research of biomorphic ceramic based on a leaf template

Abstract

Nowadays, super-hydrophobic surface has aroused the science researchers’ close attention due to its unique properties of self-cleaning、corrosion prevention、microfluid system、biology compatibility and its potential applications in national defence、industry and agriculture、dailylife. It is a new concept of material preparation that making direct use of nature plenty of biological template with special structure and function after long-term evolution to produce new inorganic material which possess the biological structure and replacing high temperature resistance、flexible nanostructures organic composition by stable、high temperature resistance、high hardness inorganic material. This research fabricate ceramic of ZnO/C which based on plants leaves template and analysis the surface morphology、chemical composition and superhydrophobicity. The CA of the ZnO/C ceramic is more than 150°,which proved it has the property of superhydrophobicity.

Keywords superhydrophobicity plant-template Zinc oxide fabricate

毕业设计说明书（论文）中文摘要 I

毕业设计说明书（论文）外文摘要 II

第一章绪论 2

1.1 超疏水概述 2

1.1.1 植物叶片的超疏水现象及表面特征 2

1.2 超疏水模型及机理 4

1.3 超疏水材料的制备方法及应用 5

1.4本课题的研究内容及其意义 8

第二章实验部分 8

2.1 实验材料及设备 8

2.1.1 实验材料 8

2.1.2 实验设备 8

2.2 实验方案设计 8

2.3 实验制备过程 9

2.3.1 以荷叶为模板ZnO/C陶瓷的制备 9

2.3.2 以粽叶为模板ZnO/C陶瓷的制备 10

2.4 超疏水ZnO/C表面的表征 11

第三章实验结果和讨论 12

3.1以荷叶为模板制备ZnO/C陶瓷 12

3.1.1 晶体结构分析 12

3.1.2 表面形态和成分分析 13

3.1.3 红外分析 15

3.1.4 超疏水性能 16

3.2 以棕叶为模板ZnO/C陶瓷陶瓷的表征分析 ZnO/C陶瓷植物叶片模板的超疏水陶瓷的制备及性能研究:http://www.751com.cn/cailiao/lunwen_75358.html