摘要本文主要针对在铝基体上采用钢焊丝+铝镁焊丝获得铁铝堆焊层，通过调节焊接工艺参数，使Fe-Al堆焊层成形良好，无气孔、裂纹、夹杂等缺陷出现，使Fe-Al合金主要成分为Fe3Al。

铁铝堆焊的焊缝以柱状晶存在，且其中含有大量的析出相，当钢焊丝的送丝速度为8m/min,铝焊丝的送丝速度为4.5m/min时，焊缝成形良好，硬度在370HV左右，与Fe3Al化合物的硬度很接近，说明焊缝层中存在Fe3Al。67488

毕业论文关键词： Fe-Al堆焊层，双丝焊工艺，显微组织，硬度

毕业设计说明书（论文）外文摘要

Abstract  This article mainly aims at on the aluminum substrate by using steel wire + aluminum magnesium iron wire for hardfacing layer, by adjusting the welding process parameters, make the Fe - Al surfacing layer forming good, without defects such as porosity, crack, inclusion, the main ingredients of Fe3Al Fe - Al alloy.

Iron and aluminum welding the weld to the existence of the columnar crystal, and contains a large number of precipitated phase, when the steel wire of the wire feeding speed is 8 m/min, weld wire wire feed speed of 4.5 m/min, the weld is good, the hardness is controlled in 370 hv, and the hardness of Fe3Al compounds is very close to that of weld layers exist in the Fe3Al.

Keyword:Fe-Al surfacing layer, double wire welding process, the microstructure and hardness

1绪论 6

1.1 本课题的研究意义和内容 6

1.1.1  本课题的研究意义 6

1.1.2本课题的研究内容 6

1.2  Fe-Al 金属间化合物研究概况与发展方向 6

1.2.1 Fe-Al金属间化合物室温脆性本质 6

1.2.2  合金化 7

1.3  Fe-Al合金层的制备方法和局限性 7

1.3.1高速电弧喷涂技术 7

1.3.2 激光熔敷技术 7

1.3.3 等离子喷涂技术 8

1.4  双丝焊分类及其特点 8

1.4.1　双丝焊的研究状况 8

1.4.2 　双丝焊的优点及其应用 9

2  铝钢异种金属双丝焊试验设备及材料 10

2.1  法国SAF公司的R450双丝焊机工作原理 10

2.2  实验设备 11

2.2.1  法国SAF公司的双丝焊接系统双丝焊焊接系统组成 11

2.2.2  金相显微境 12

2.3  试验材料 13

2.3.1  母材 13

2.3.2  焊丝牌号 13

2.3.3  保护气体 13

3  试验方案设计及分析 14

3.1  焊接操作过程 14

3.2  试验结果 14

4  金相实验 16

4.1  金相实验步骤 16

4.2 试样宏观分析 16

4.2.1  5mm铝板表面堆铁铝 16

4.2.2  5mm铝板表面堆铁后，再堆铁铝 铝表面堆焊Fe-Al合金层的组织性能研究:http://www.751com.cn/cailiao/lunwen_75707.html